W-Nr 1.7337 | 16CrMo4.4 Bars UT Test
Alloy structural steel are widely used in the filed of ship, vehicle, airplane, guided missile, weapons, railway, bridges, pressure vessel, machine tools, mechanical components with a bigger sectional size and so on.
| Product parameters | |
| Material Technical Standards:: | DIN EN 10028-2, DIN 17755-83 |
| Melting Process Route:: | EAF + VD + LF / BEF + ESR |
| Min. order quantity Per Batch:: | 1300 KG |
| Heat Treatment Practice:: | Quenched 930 ℃, water, oil or air cooled, Tempered 680 ℃, air cooled |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 55 days after 30% deposit prepayable |
Description
| C (％) | 0.13 ～ 0.20 |
| Si(％) | 0.15 ～ 0.35 |
| Mn(％) | 0.50 ～ 0.80 |
| P(％) | ≤ 0.035 |
| S (％) | ≤ 0.035 |
| Cr (％) | 0.90 ～ 1.20 |
| Ni (％) | ≤ 0.40 |
| Mo(％) | 0.40 ～ 0.60 |
| Other (％) | - |
| Condition of heat treatment | - |
| Tensile Rm (MPa) | 540 ～ 690 |
| Yield Rp0.2 (MPa) | 345 |
| Elongation A (%) | 20 |
| Reduction in cross section on fracture Z (%) | - |
| Impact AKV/AKU (J) | 41 |
| Brinell Hardness (HBW) | 160 ～ 205 |
| The alloy is usually produced by BEF & EAF followed by electroslag remelting (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements. Bars are usually supplied black/bright in the annealed condition. |
Shapes and Dimensions: Round bar (Diameter): 5.50 ~ 650mm Square bar / Flat bar: 3 ~ 650mm Wire rod (Diameter): 0.10 ~ 16mm Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form) Forging piece: Different shapes based on OEM |