EN 10083-2 type 36NiCrMo16 Round bar
| Product parameters | |
| Material Category:: | 3.8Ni-1.8Cr-Mo Base Structural Steel |
| Material Technical Standards:: | DIN EN 10083-2 |
| Terms of Price:: | Ex works, CIF, CFR |
| Stocklist & Inventory Available:: | Diameter 55mm / 65mm / 100mm / 130mm |
| Min. order quantity Per Batch:: | 200 KG per bill |
| Product Shapes:: | Round bar |
| Customs HS code:: | 72284000 |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 5 days after 30% Deposit. |
| Unified Social Credit Code:: | 91510871777942750J |
Description
MATERIAL CATEGORY - hardened and tempered steel
PRODUCT DESCRIPTION
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.32 ~ 0.39
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.50 ~ 0.80
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 1.60 ~ 2.00
Molybdenum, Mo (％): 0.25 ~ 0.45
Nickel, Ni (％): 3.60 ~ 4.10
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 830~850oil
Heat treatment temperature /℃| Tempering : 450~650
Hardness after annealing ≤HBS: 265
Steel dimension /mm: 41 - 100
|σb≥/MPa: 1270 ~ 1470
|σs≥/MPa: 1030
|δ5≥/(%): 7.0
|ψ≥/(%): 40.0
|AKV≥/J: 20
PRODUCT DESCRIPTION
Bars are usually supplied bright in the annealed condition, or bright annealing specially.
Final heat treatment - Quenched and tempered.
MATERIAL SPECIFICATIONS - DIN EN 10083-2 (2006), DIN 17200 (1987)
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): 0.32 ~ 0.39
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.50 ~ 0.80
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 1.60 ~ 2.00
Molybdenum, Mo (％): 0.25 ~ 0.45
Nickel, Ni (％): 3.60 ~ 4.10
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature /℃: 1050～850
Heat treatment temperature /℃| annealing: 650～700
Heat treatment temperature /℃| Normalizing: 850～880
Heat treatment temperature /℃| Quenching: 830~850oil
Heat treatment temperature /℃| Tempering : 450~650
Hardness after annealing ≤HBS: 265
Steel dimension /mm: 41 - 100
|σb≥/MPa: 1270 ~ 1470
|σs≥/MPa: 1030
|δ5≥/(%): 7.0
|ψ≥/(%): 40.0
|AKV≥/J: 20