TECHNICAL DATA SHEET - ASTM A514 Grade S
MATERIAL CATEGORY - low alloy Series steel
MATERIAL SPECIFICATIONS - ASTM A514
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.11 ~ 0.21
Si (％): 0.15 ~ 0.40
Mn (％): 1.10 ~ 1.50
P (％)≤: 0.030
S (％)≤: 0.025
Cr (%): -
Ni (%): -
Mo (%): 0.10 ~ 0.60
V (%): ≤ 0.06
B (%): 0.001 ~ 0.005
Nb (%): ≤ 0.06
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/MPa: 760
Yield strength, σ0.2/MPa: 690
Elongation, δ(％): 18.0
Reduction of area, ф(％): -
Hardness (HBW): 293 max.
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5 to 450mm
Flat bar / steel strip: THK0.15 ~ 350 X W10 ~ 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL(sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL CATEGORY - low alloy Series steel
MATERIAL SPECIFICATIONS - ASTM A514
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.11 ~ 0.21
Si (％): 0.15 ~ 0.40
Mn (％): 1.10 ~ 1.50
P (％)≤: 0.030
S (％)≤: 0.025
Cr (%): -
Ni (%): -
Mo (%): 0.10 ~ 0.60
V (%): ≤ 0.06
B (%): 0.001 ~ 0.005
Nb (%): ≤ 0.06
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/MPa: 760
Yield strength, σ0.2/MPa: 690
Elongation, δ(％): 18.0
Reduction of area, ф(％): -
Hardness (HBW): 293 max.
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF).
For a purpose of superior quality, it should be smelt via technology of Electroslag remelting or vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5 to 450mm
Flat bar / steel strip: THK0.15 ~ 350 X W10 ~ 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.