1.3811 Non-magnetic Steel Stock Available
| Product parameters | |
| Material Category:: | Austenitic Non-magnetic Stainless Steel |
| Material Technical Standards:: | DIN SEW 390 (1991) |
| Min. order quantity Per Batch:: | 1300 KG |
| Product Shapes:: | Round bars, flat bars, forgings, ring |
| Production Lead Time:: | Within 45 days after 30% deposit prepayable |
| Company ISO Register No:: | UQ211218R0 |
Description
RAW MATERIAL DATASHEET - Grade DIN 1.3811
Material Catetory - Non-magnetic stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Main Chemical Elements (mass weight - %)
Carbon, C (％): ≤ 0.15, Silicon, Si (％): ≤ 1.00, Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.060, Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 24.0 ~ 26.0, Nickel, Ni (％): ≤ 0.50, Molybdenim, Mo (％): -
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Soft annealing treatment temperature: 800 ~ 860 ℃
Tensile strength, σb≥ /MPa: 450 ~ 760
Yield strength, σ0.2 ≥/MPa: 255
Elongation, δ≥(％): 15.0
Impact strength, Akv ≥/J: -
Material Catetory - Non-magnetic stainless steel and alloy
Material Specifications - DIN SEW 390 (1991)
Main Chemical Elements (mass weight - %)
Carbon, C (％): ≤ 0.15, Silicon, Si (％): ≤ 1.00, Manganese, Mn (％): ≤ 1.00
Phosphorus, P (％) ≤: 0.060, Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 24.0 ~ 26.0, Nickel, Ni (％): ≤ 0.50, Molybdenim, Mo (％): -
HOT WORKING, HEAT TREATMENT AND MECHANICAL PROPERTIES
Hot working temperature: 1150 ~ 850℃
Soft annealing treatment temperature: 800 ~ 860 ℃
Tensile strength, σb≥ /MPa: 450 ~ 760
Yield strength, σ0.2 ≥/MPa: 255
Elongation, δ≥(％): 15.0
Impact strength, Akv ≥/J: -