S17400 Turbine blade steels
| Product parameters | |
| Material category:: | Precipitation hardening steel |
| Material technical standards:: | ASTM A693, ASTM A705 |
| Stock & Inventory available:: | Round bar 3.0 ~ 300mm |
| Certification:: | MTR, COC, Certificate of origin, Form A/E, Invoice, Packing list |
| Production lead time:: | Within 5 days after payment |
| Unified social credit code:: | 91510871777942750J |
Description
Introduction:
S17400 is a corrosion resistant grade which is soft and ductile in the solution annealed condition. Medium to high strength, good toughness and strength is obtained by the appropriate ageing treatment. As a martensitic precipitation hardening stainless it is characterised by high tensile strength and high yield strength obtained by solution annealing, followed by a single or double low temperature age hardening treatment. AMS 5643 has corrosive properties comparable to 304 austenitic stainless steel in many environments.
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
S17400 is a corrosion resistant grade which is soft and ductile in the solution annealed condition. Medium to high strength, good toughness and strength is obtained by the appropriate ageing treatment. As a martensitic precipitation hardening stainless it is characterised by high tensile strength and high yield strength obtained by solution annealing, followed by a single or double low temperature age hardening treatment. AMS 5643 has corrosive properties comparable to 304 austenitic stainless steel in many environments.
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace. AMS 5643 is used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace. AMS 5643 is used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Technical Standard: AMS 5643
Equivalent
| DIN | ASTM | AISI | UNS | JIS | Other |
|---|---|---|---|---|---|
| 1.4542 X5CrNiCuNb16-4 |
Grade 630 | 630 | S17400 | SUS 630 | 17-4PH AMS 5643 AMS 5622 Z6CNU17-04 10705GU-GV |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.07 | ≤ 1.00 | ≤ 1.00 | ≤ 0.040 | ≤ 0.030 | 15.0 ～ 17.0 | 3.00 ～ 5.00 | - | Cu 3.00 ～ 5.00 Nb+Ta 0.15 ～ 0.45 |
Typical Mechanical Properties
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealed | ≤ 1034 | ≤ 650 | 6.0 ～ 15.0 | 30.0 ～ 60.0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14.0 | ≥ 50.0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14.0 | ≥ 54.0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15.0 | ≥ 56.0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16.0 | ≥ 58.0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17.0 | ≥ 58.0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19.0 | ≥ 60.0 | ≥ 68 | ≤ 311 |
| H1150+H1150 | ≥ 965 | ≥ 760 | ≥ 20.0 | ≥ 60.0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22.0 | ≥ 68.0 | ≥ 135 | ≤ 277 |