AMS 5654 ESR Quality Austenitic Stainless Steel Bars
| Product parameters | |
| Material Category:: | Austenitic Stainless Steel |
| Material Technical Standards:: | AMS 5654F |
| Place of Origin: | P. R. China |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Round bar Diam. 20 ~ 210mm |
| Min. order quantity Per Batch:: | 1000 KG |
| Product Shapes:: | Round bar, Flat bar, Plate |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on. These products have been used typically for parts requiring corrosion and heat resistance and subject to very rigid inspection standards, especially when such parts are welded during fabrication, for parts requiring oxidation resistance up to 1500 °F (816 °C)
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Square bar / Flat bar (Thickness X width): 10 to 610mm
Wire rod (Diameter): 1.0 to 13.0mm
Steel strip: THK0.5 ~ 3.0, width 10 ~ 1200mm
Length: fixed length, random length or based on the customer's special requirement.
CHEMICAL COMPOSITIONS (mass weight %)
C (％): ≤ 0.08, Mn (％): ≤ 2.00, Si (％): ≤ 1.00
P (％)≤: 0.020, S (％)≤: 0.020
Cr (％): 17.0 ~ 19.0, Ni (％): 9.00 ~ 13.0, Nb (%): 10 X C ~ 1.10,
Mo (%): ≤ 0.75, Cu (%): ≤ 1.00, Fe (%): balance.
Mechanical Properties at room temp.
Shapes: bars, wire, and forgings
Tensile strength, σb/MPa: 517
Tensile strength, σb/MPa: 862 max. (wire rod)
Yield strength, σ0.2/MPa: 207
Elongation, δ(％): 30.0
Reduction of area, ф (％): 40.0
Hardness under solution condition | HBW: 255 Max.