1.4939 Forgings, X11CrNiMoN12 Blade Steels
DIN 1.4939 (X11CrNiMoN12), A Martensitic Stainless Steel also known as XM-32, AMS 1.4938, S64152, X12CrNiMoV12-3,,, Equivalent standards are similar to one or more standards provided by the supplier.
Product parameters | |
Material Category:: | Martensitic Stainless Steel Series |
Stocklist & Inventory Available:: | Diameter 55 ~ 210mm |
Melting Process Route:: | EF + VD + ESR |
Min. order quantity Per Batch:: | one bar |
Production Lead Time:: | Within 5 days after 30% downpayment. |
Company ISO Register No:: | UQ211218R0 |
Description
Introduction:
AMS 1.4939 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.1.4938 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.1.4938 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
DIN | W-Nr | AMS |
---|---|---|
X11CrNiMoN12 | W-Nr 1.4938 | 1.4939 |
Chemical Composition (Mass weight %)
C | Si | Mn | P | S | Cr | Ni | Mo | Other |
---|---|---|---|---|---|---|---|---|
0.08 ~ 0.15 | ≤ 0.50 | 0.40 ~ 0.90 | ≤ 0.025 | ≤ 0.015 | 11.0 ~ 12.5 | 2.00 ~ 3.00 | 1.50 ~ 2.00 | V 0.25 ~ 0.40 V 0.010 ~ 0.040 |
Mechanical Properties under room temp.
Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
---|---|---|---|---|---|---|
Annealing | - | - | - | - | - | - |
Q/T | 950 ~ 1150 | ≥ 800 | ≥ 13.0 | - | ≥ 55 | - |