Specifications EN 58A Datasheet, Stocklist EN 58A Chemical, Inventory EN 58A Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materi
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | EN 58A |
| Material Technical Standards:: | BS |
| Specification Code:: | BS970 Part 6 |
| Place of Origin: | England |
Description
TECHNICAL DATA SHEET - Grade EN 58A
MATERIAL CATEGORY - Stainless steel 18%Cr / 8.0Ni
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.12 ~ 0.20
Mn (％): 1.70 ~ 2.50
Si (％): 0.20 Min.
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 7.00 ~ 10.0
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 515
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 40.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB215
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 520mm
Square bar / Flat bar: 10mm to 600mm
Rolled / forged plate: 10mm to 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
MATERIAL CATEGORY - Stainless steel 18%Cr / 8.0Ni
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.12 ~ 0.20
Mn (％): 1.70 ~ 2.50
Si (％): 0.20 Min.
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 7.00 ~ 10.0
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 515
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 40.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB215
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 520mm
Square bar / Flat bar: 10mm to 600mm
Rolled / forged plate: 10mm to 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com