F50 Duplex Stainless Steel Bars.
| Product parameters | |
| Material Category:: | Duplex Stainless Steel |
| Specification Code:: | ASTM A182 - 2018 |
| Place of Origin: | P. R. China |
| Standard Export Packing Way:: | Wooden box, wooden Pallet / tray with free from fumigation. |
| Production Lead Time:: | Within 75 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
TECHNICAL DATASHEET - ASTM A182 Grade F50
Material Technical Standards - ASTM A182 - 2018
Steel Material Type - 25Cr-6Ni-2Mo Ferritic - Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
Stocklist & Inventory - Diameter 18mm ~ 100mm
Chemical Composition (mass weight % )
C (％): ≤ 0.030, Mn (％): ≤ 2.00, Si (％): ≤ 1.00, P (％)≤: 0.045, S (％)≤: 0.030
Ni (%): 5.50 ~ 6.50, Cr (%): 24.0 ~ 26.0, Mo (%): 1.20 ~ 2.00
N (%): 0.14 ~ 0.20, Fe (%): Remainder.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/MPa: 450
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1050 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1200mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Material Technical Standards - ASTM A182 - 2018
Steel Material Type - 25Cr-6Ni-2Mo Ferritic - Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
Stocklist & Inventory - Diameter 18mm ~ 100mm
Chemical Composition (mass weight % )
C (％): ≤ 0.030, Mn (％): ≤ 2.00, Si (％): ≤ 1.00, P (％)≤: 0.045, S (％)≤: 0.030
Ni (%): 5.50 ~ 6.50, Cr (%): 24.0 ~ 26.0, Mo (%): 1.20 ~ 2.00
N (%): 0.14 ~ 0.20, Fe (%): Remainder.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/MPa: 450
Elongation, δ ≥(％): 25.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1050 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T10 ~ 400mm X W60 ~ 1200mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.