L-605
Specifications L-605 datasheet, L-605 Chemical, L-605 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conf
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | L-605 |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 5537G |
| Place of Origin: | USA |
Description
MATERIAL TECHNICAL STANDARD - Grade L-605
MATERIAL CATEGORY - high alloy stainless Steel Series
TECHNICAL SPECIFICATION - AMS 5537G
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.05 ~ 0.15
Mn (％): 1.00 ~ 2.00
Si (％): ≤ 0.40
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 19.0 ~ 21.0
Ni (％): 9.00 ~ 11.0
W (%): 14.0 ~ 16.0
Co (%): Remainder
Fe (%): ≤ 3.00
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: plate, sheet, strip
Tensile strength, σb/MPa: 895
Yield strength, σ0.2/MPa: 375
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness (HB): 229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), BEF (AOD) & VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 400mm
Square bar / Flat bar: 10mm to 600mm
Wire rod: 1.0mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
MATERIAL CATEGORY - high alloy stainless Steel Series
TECHNICAL SPECIFICATION - AMS 5537G
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.05 ~ 0.15
Mn (％): 1.00 ~ 2.00
Si (％): ≤ 0.40
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): 19.0 ~ 21.0
Ni (％): 9.00 ~ 11.0
W (%): 14.0 ~ 16.0
Co (%): Remainder
Fe (%): ≤ 3.00
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: plate, sheet, strip
Tensile strength, σb/MPa: 895
Yield strength, σ0.2/MPa: 375
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness (HB): 229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), BEF (AOD) & VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 400mm
Square bar / Flat bar: 10mm to 600mm
Wire rod: 1.0mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com