EN 60 Martensitic Stainless Steel Bars
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | EN 60 |
| Specification Code:: | BS EN 10088-3 |
| Place of Origin: | P. R. China |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Round bar Diam. 50mm / 60mm / 120mm |
| Min. order quantity Per Batch:: | 1300 KG |
| Ultrasonic Test Standard:: | / GB/T 4162 / EN 10228-3 / EN 10308. |
| Production Lead Time:: | Within 55 days after 40% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
MATERIAL CATEGORY - Stainless steel 17%Cr / 0.25%Ni
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): ≤ 0.12, Mn (％): ≤ 1.00, Si (％): ≤ 1.00
P (％)≤: 0.035, S (％)≤: 0.025
Cr (%): 16.0 ~ 18.0, Ni (%): ≤ 0.50, Mo (%): -
Fe (%): balance.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:
Tempering temperature /℃:
Tensile strength,σb/≥ MPa: 450
Yield strength, σ0.2/≥ MPa: 205
Elongation, δ ≥(％): 22.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB225
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 550mm
Rolled / forged plate: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.