NCF625
Specifications NCF625 Datasheet, NCF625 Chemical, Alloy NCF625 Properties forgings, Technical specifications - KS D3531 - 2003. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | NCF625 |
| Material Technical Standards:: | KS |
| Specification Code:: | KS D3531 - 1992/2003 |
| Place of Origin: | Korea |
Description
TECHNICAL DATA SHEET - KS D3531 Grade NCF625
TECHNICAL SPECIFICATIONS: KS D3531 - 1992/2003
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel & Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): ≥ 58.0
Cu (％): -
Al (%): ≤ 0.40
Ti (%): ≤ 0.40
Fe (%): ≤ 5.00
Mo (%): 8.00 ~ 9.00
Nb + Ta (%): 3.15 ~ 4.15
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Annealing, 870 Deg. C min. rapid colling
Tensile strength, σb/ ≥ MPa: 760
Yield strength, σ0.2/ ≥ MPa: 380
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 219 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.50 ~ 450mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@cnlhss.com
TECHNICAL SPECIFICATIONS: KS D3531 - 1992/2003
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel & Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.10
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.015
S (％) ≤: 0.015
Cr (％): 20.0 ~ 23.0
Ni (％): ≥ 58.0
Cu (％): -
Al (%): ≤ 0.40
Ti (%): ≤ 0.40
Fe (%): ≤ 5.00
Mo (%): 8.00 ~ 9.00
Nb + Ta (%): 3.15 ~ 4.15
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Annealing, 870 Deg. C min. rapid colling
Tensile strength, σb/ ≥ MPa: 760
Yield strength, σ0.2/ ≥ MPa: 380
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 219 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
AVAILABLE FORMS & DIMENSIONS
Round bar (Diameter): 5.50 ~ 450mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@cnlhss.com