TECHNICAL DATASHEET - Grade UNS S63016
MATERIAL CATEGORY - Valve steel
HS CODE - 72221100 / 72221900
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): 0.80 ~ 1.50
Mn (％): 1.00 ~ 1.80
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 20.0 ~ 23.0
Ni (％): 10.0 ~ 13.0
Mo (％): -
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Hot forming temperature /℃: 1100～980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1150～1180 Water
Heat treatment temperature and cooling method | tempered: 800~830
Mechanical property |σb/MPa: 850～1100
Mechanical property |σs≥/MPa: 550
Mechanical property |δ5≥(％): 20
Mechanical property |ψ≥(％): 30
REMELTING PROCESS
Valve steel is generally smelt in electric arc furnace EAF or AOD. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 450mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Forgings: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com
MATERIAL CATEGORY - Valve steel
HS CODE - 72221100 / 72221900
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.08 ~ 0.16
Si (％): 0.80 ~ 1.50
Mn (％): 1.00 ~ 1.80
P (％)≤: 0.045
S (％)≤: 0.030
Cr (％): 20.0 ~ 23.0
Ni (％): 10.0 ~ 13.0
Mo (％): -
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Hot forming temperature /℃: 1100～980
Heat treatment temperature and cooling method | annealed: -
Heat treatment temperature and cooling method | quenched: 1150～1180 Water
Heat treatment temperature and cooling method | tempered: 800~830
Mechanical property |σb/MPa: 850～1100
Mechanical property |σs≥/MPa: 550
Mechanical property |δ5≥(％): 20
Mechanical property |ψ≥(％): 30
REMELTING PROCESS
Valve steel is generally smelt in electric arc furnace EAF or AOD. For higher quality,it should be smelt via technology of vacuum refining and external refining.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 450mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W60 - 1000mm X L1000-12000mm
Forgings: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.