Martensitic S64152 Stainless rod, XM-32 Turbine blade Steels
Stainless steel S64152 - XM-32 is Martensitic Stainless steel that should be hardened to achieve excellent mechanical properties by different tempering temperatures. The steel achieved high strength and hardness after final tempering treatment.
| Product parameters | |
| Material Technical Standards:: | ASTM A565 / A565M |
| Stocklist & Inventory Available:: | Diameter 55 ~ 220mm |
| Min. order quantity Per Batch:: | 1300 KG |
| Mode of transportation:: | Sea shipment, Air cargo, or Courier |
| Heat Treatment Practice:: | Hardened 1050 ℃, water or oil cooled, tempered 640 ~ 690 ℃, double tempered |
| Ultrasonic Test Standard:: | EN 10308, MIL-STD-AMS 2154 CLa |
| Production Lead Time:: | Within 45 days after 30% deposit prepayable |
Description
| C (％) | ≤ 0.15 |
| Si(％) | ≤ 1.00 |
| Mn(％) | ≤ 2.00 |
| P(％) | ≤ 0.04 |
| S (％) | 0.12 ～ 0.25 |
| Cr (％) | 17.0 ～ 19.0 |
| Ni (％) | 8.00 ～ 10.0 |
| Mo(％) | ≤ 0.60 |
| Other (％) | Pb 0.12 ～ 0.30 |
| Condition of heat treatment | - |
| Tensile Rm (MPa) | - |
| Yield Rp0.2 (MPa) | - |
| Elongation A (%) | - |
| Reduction in cross section on fracture Z (%) | - |
| Impact AKV/AKU (J) | - |
| Brinell Hardness (HBW) | - |
| The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3. Bars are usually supplied black/bright in the annealed condition. |
Forms and Dimensions Available Round bar (Diameter): 5.50 ~ 650mm Square bar / Flat bar: 3 ~ 650mm Wire rod (Diameter): 0.10 ~ 16mm Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form) Forging piece: Different shapes based on OEM |