W-Nr 1.4105 Ferritic Stainless Steel
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.W-Nr 1.4105 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
| Product parameters | |
| Material Technical Standards:: | DIN EN 10088-1, 10088-4, 10297, 10312 |
| Min. order quantity Per Batch:: | 3300 KG |
| Heat Treatment Practice:: | Annealed 750 ~ 850℃, water or air cooled |
| Ultrasonic Test Standard:: | EN 10228-3, GB/T 4162-2008, ASTM E2375, ASTM A745. EN 10307-2001 |
| Production Lead Time:: | Within 55 days after 40% deposit prepayable |
Description
W-Nr 1.4105 is usually produced by BEF & AOD.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
All Grades Equivalents
| DIN | W-Nr |
|---|---|
| X6CrMoS17 | W-Nr 1.4105 |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.08 | ≤ 1.50 | ≤ 1.50 | ≤ 0.040 | 0.15～ 0.35 | 16.0 ～ 18.0 | - | 0.20 ～ 0.60 | - |
Typical Mechanical Properties
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | 430 ～ 630 | ≥ 250 | ≥ 20.0 | - | - | ≤ 220 |
| H/T | - | - | - | - | - | - |
Shapes / Dimensions:
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.