Aerospace AMS 5629 Martensitic Stainless Bars
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
| Product parameters | |
| Material Technical Standards:: | ASTM A693, AMS 5929G |
| Stocklist & Inventory Available:: | Diameter 105 / 120mm, Flat bar 65 X 600 X Lmm |
| Surface Condition:: | Cold machined, bright |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 35 days after 40% deposit prepayabl3 |
Description
Special Meleting Process
Applications
Referenced Relevant Standards
ASTM A370 Mechanical Testing of Steel Products.
ASTM A604 Macroetch Testing of Consumable Electrode Remelted Steel Bars and Billets.
ASTM E112 Determining Average Grain Size.
ASTM E353 Chemical Analysis of Stainless,Heat-Resisting,Maragingand Other Similar Chromium-Nickel-lron Alloys.
Chemical compositions (Mass Weight - %)
C (％): ≤ 0.05, Si (％): ≤ 0.10, Mn (％): ≤ 0.10, P (％) ≤: 0.010, S (％) ≤: 0.008
Cr (％): 12.25 ~ 13.25, Ni (％): 7.50 ~ 8.50, Al (%): 0.90 ~ 1.35
Mo (%): 2.00 ~ 2.50, N (%): ≤ 0.010, Fe (%): balance
Typical Mechanical Properties
Shapes: bar, flat bars and forgings
Heat treatment condition: H1150 (620℃)
Tensile strength, σb/MPa: 1207 MPa Max. for wire
Tensile strength, σb/MPa: 930
Yield strength, σ0.2/MPa: 620
Elongation, δ(％): 14.0
Reduction of area, ф (％): 50.0
Hardness under annealed condition | HBW: 363 max.
This alloy is generally smelt in VOD or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
These products have been used typically for parts requiring corrosion resistance,stress-corrosion resistance, high strength up to 600F(316C),and good ductility and strength in the transverse direction in large section sizes, but usage is not limited to such applications.