AMS 5646 / S34700 Austenitic Stainless Steel
Stock over 60 grades with a competitive price, along with cutting service for specific requirement. Customizing special material is welcome.
| Product parameters | |
| Material Technical Standards:: | ASTM A276 |
| Place of Origin: | P.R. China |
| Stocklist & Inventory Available:: | Diameter 15 ~ 230mm |
| Min. order quantity Per Batch:: | 1000 KG |
| Production Lead Time:: | Within 25 days after 40% deposit prepayable |
| Company ISO Register No:: | UQ211218R0 |
APPLICATIONS
These products have been used typically for parts requiring good corrosion resistance and which will be subjected to elevated temperatures during fabrication or in service and for parts requiring oxidation resistance up to 1500 °F (816 °C),
Special Melting Process
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD) or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement. It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
Chemical Elements (mass weight %)
C (％): ≤ 0.08, Mn (％): ≤ 2.00, Si (％): ≤ 1.00, P (％)≤: 0.040, S (％)≤: 0.030
Cr (％): 16.0 ~ 19.0, Ni (％): 9.00 ~ 12.0, Nb (%): 10 x C ~ 1.10
Mo (%): ≤ 0.75, Cu (%): ≤ 0.75, Co (%): ≤ 1.00, Fe (%): balance
Mechanical Properties under Room Temperature
Shapes: bars and forgings
Tensile strength, σb/MPa: 517
Tensile strength, σb/MPa: 585 ~ 862 (wire rod)
Yield strength, σ0.2/MPa: 207
Elongation, δ(％): 30.0
Reduction of area, ф (％): 40.0
Hardness under aged condition | HBW: -
Hardness under solution condition | HBW: 255 Max.
Shapes and Dimensions
Round bar (Diameter): 5.5 to 530mm
Square bar / Flat bar (Thickness X width): 10 to 650mm
Wire rod (Diameter): 3.0 to 13.0mm
Steel strip: THK0.5 ~ 3.0, Width 10 ~ 220mm
Length: Fixed length or random length or based on the customer's special requirement.