FXM-19 Austenitic Stainless Steel
Inventory FXM-19 Specifications Stock Datasheet Chemical, Exporters FXM-19 Properties Flat Bar Forging Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards - ASTM A182 - 2018.or by agreement.
| Product parameters | |
| Material Technical Standards:: | ASTM A182 |
| Stocklist & Inventory Available:: | Diameter 35 ~ 150mm |
| Min. order quantity Per Batch:: | 500 kg per diameter |
| Certification:: | MTR, COC, Certificate of origin, Form A/E, Invoice, Packing list |
| Production Lead Time:: | Within 25 days after 40% deposit prepayable |
Description
Austenitic Non-magnetic Stainless Steel FXM-19 can be used in a wide variety of industries including chemical, marine, nuclear, food processing, petrochemical, sour well service, cryogenic, textile and pulp & paper.
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 300mm
Square bar / Flat bar: 10mm to 600mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Chemical Compositions (Mass weight %) - Grade FXM-19
C (％): ≤ 0.06, Mn (％): 4.00 ~ 6.00, Si (％): ≤ 1.00, P (％)≤: 0.040, S (％)≤: 0.030
Ni (%): 11.50 ~ 13.5, Cr (%): 20.5 ~ 23.5, Mo (%): 1.50 ~ 3.00, Nb (%): 0.10 ~ 0.30
N (%): 0.20 ~ 0.40, V (%): 0.10 ~ 0.30
Typical Mechanical Properties
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/MPa: 380
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 55.0
Hardness via heat treatment /HBW: -
Heat Treatment Practice
Condition: solution annealing (+AT)
Cooling medium: water or oil cooling
Tempering temperature: 1040℃