ASTM A565 Grade 616 Round bar Available Stock
| Product parameters | |
| Material Category:: | Martensitic Stainless Steel Series |
| Material Technical Standards:: | ASTM A565 |
| Terms of Price:: | Ex works, CIF, CFR |
| Stocklist & Inventory Available:: | Diameter 20 ~ 230mm |
| Melting Process Route:: | BEF + AOD / +ESR |
| Min. order quantity Per Batch:: | 500 KG |
| Customs HS code:: | 722211 / 722230 |
| Heat Treatment Practice:: | Hardened 1030 ℃, water or air cooled, tempered 650 ℃ min, double tempered |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 25 days after 30% deposit prepayable |
| Company ISO Register No:: | UQ211218R0 |
- ASTM A565 A565M Material Datasheet PDFDownload
Description
ASTM A565 Grade 616, A Martensitic Stainless Steel also known as AISI 422, DIN 1.4935, JIS SUH616, ASTM B4B,,, Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.
Chemical Elements Weight (%): Grade ASTM A565 Grade 616
C (％): 0.20 ~ 0.25, Si (％): ≤ 0.50, Mn (％): ≤ 1.00, P (％)≤: 0.025, S (％)≤: 0.020
Cr (％): 11.0 ~ 12.5, Ni (％): 0.50 ~ 1.00, Mo (％): 0.90 ~ 1.25, V (％): 0.20 ~ 0.30
W (%): 0.90 ~ 1.25, Fe (%): Balance
Mechanical Properties Under Room Temperature
Form: bar, flat bar, forgings
Condition + H: Tempering (620℃)
Tensile strength, σb/MPa: 965 min.
Yield strength, σ0.2/MPa: 760 min.
Elongation, δ (％): 13.0 min
Reduction of area, ф (％): 30.0
Hardness | HRB: 302 ~ 352
Condition + HT: Tempering (675℃)
Tensile strength, σb/MPa: 825 min.
Yield strength, σ0.2/MPa: 685 min.
Elongation, δ (％): 17.0 min.
Reduction of area, ф (％): 35.0 min.
Hardness | HRB: 241 ~ 285