STR 409L
Specifications STR 409L Datasheet, Chemical STR 409L, Grade STR 409L Properties forging Bar Plate machined, Technical specifications - KS D3731 - 2002 / 2007. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straighte
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | STR 409L |
| Material Technical Standards:: | KS |
| Specification Code:: | KS D3732 |
| Place of Origin: | Korea |
Description
TECHNICAL DATA SHEET - KS D3732 Grade STR 409L
TECHNICAL SPECIFICATIONS: KS D3732 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 10.5 ~ 11.75
Ni (％): ≤ 0.60
Mo (%): -
N (%): -
Ti (%): 6 X C ~ 0.75
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Annealing, 780 ~ 950 slow colling
Tensile strength, σb/ ≥ MPa: 360
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (％) ≥: 22.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 165 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 450mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 610mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
TECHNICAL SPECIFICATIONS: KS D3732 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 10.5 ~ 11.75
Ni (％): ≤ 0.60
Mo (%): -
N (%): -
Ti (%): 6 X C ~ 0.75
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Annealing, 780 ~ 950 slow colling
Tensile strength, σb/ ≥ MPa: 360
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (％) ≥: 22.0
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 165 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 450mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 610mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar