| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | STR 600 |
| Material Technical Standards:: | KS |
| Specification Code:: | KS D3731 - 2002/2007 |
| Place of Origin: | Korea |
Description
TECHNICAL DATA SHEET - KS D3731 Grade STR 600
TECHNICAL SPECIFICATIONS - KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.15 ~ 0.20
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 10.0 ~ 13.0
Ni (％): ≤ 0.60
Mo (%): 0.30 ~ 0.90
Nb (%): 0.20 ~ 0.60
V (%): 0.10 ~ 0.40
N (%): 0.10 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1100 ~ 1170 Deg.C
Aged 600 Deg. C min., air cooling
Tensile strength, σb/ ≥ MPa: 835
Yield strength, σ0.2/ ≥ MPa: 385
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 30.0
Hardness ≤ (HBW): 321 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com
TECHNICAL SPECIFICATIONS - KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Heat resistant stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.15 ~ 0.20
Si (％): ≤ 0.50
Mn (％): 0.50 ~ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 10.0 ~ 13.0
Ni (％): ≤ 0.60
Mo (%): 0.30 ~ 0.90
Nb (%): 0.20 ~ 0.60
V (%): 0.10 ~ 0.40
N (%): 0.10 ~ 0.40
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated 1100 ~ 1170 Deg.C
Aged 600 Deg. C min., air cooling
Tensile strength, σb/ ≥ MPa: 835
Yield strength, σ0.2/ ≥ MPa: 385
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 30.0
Hardness ≤ (HBW): 321 Max.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com