W-Nr 1.4000
Stainless steels. List of stainless steels
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | W-Nr 1.4000 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN EN 10088-1 |
| Place of Origin: | Germany |
Description
Introduction:
W-Nr 1.4000 is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
W-Nr 1.4000 is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
W-Nr 1.4000 The chromium content is or so 12% ~ 30%, its corrosion resistance, toughness and weldability improve along with the increase of chromium content. Chloridum stress corrosion resistance is superior to other types of stainless steels. Corrosion resistance and oxidatio resistance of ferritic stainless steel are pretty well due to its high chromium content, but possess lower mechanical property and processing property. they are widely used in lower stress acidproof structure and oxidation resistant steels, which can resist the corrosion from atmosphere, nitric acid, and saline solution, and also possess excellent property of high temperature oxidation resistance, lower coefficient of thermal expansion. are used in the application of nitric acid and foodstuffs factory equipments, mechanical components at high working temperature,such as mechanical parts for combustion gas turbine.
W-Nr 1.4000 The chromium content is or so 12% ~ 30%, its corrosion resistance, toughness and weldability improve along with the increase of chromium content. Chloridum stress corrosion resistance is superior to other types of stainless steels. Corrosion resistance and oxidatio resistance of ferritic stainless steel are pretty well due to its high chromium content, but possess lower mechanical property and processing property. they are widely used in lower stress acidproof structure and oxidation resistant steels, which can resist the corrosion from atmosphere, nitric acid, and saline solution, and also possess excellent property of high temperature oxidation resistance, lower coefficient of thermal expansion. are used in the application of nitric acid and foodstuffs factory equipments, mechanical components at high working temperature,such as mechanical parts for combustion gas turbine.
All Grades Comparison
| DIN | W-Nr |
|---|---|
| X6Cr13 | W-Nr 1.4000 |
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.08 | ≤ 1.00 | ≤ 1.00 | ≤ 0.040 | ≤ 0.015 | 12.0 ～ 14.0 | - | - | - |
Mechanical Properties
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | - | - | - | - | - | - |
| Q/T | 550 ～ 700 | ≥ 400 | ≥ 18.0 | - | - | - |
Forms and Shapes:
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Length: Fixed length or random length or based on the customer's special requirement.
For all stock availability contact Sales.