X11CrNiMoN12 Available Stock Round bar
| Product parameters | |
| Material Category:: | Martensitic Stainless Steel Series |
| Material Technical Standards:: | DIN EN 10302 / 10269, DIN 17742, EN 10095 |
| Stocklist & Inventory Available:: | Diameter 55 ~ 320mm |
| Min. order quantity Per Batch:: | 500 KG |
| Certification:: | Commercial Invoice, Packing list, CO, Bill of lading, Origin of Certificate, Form E |
| Customs HS code:: | 72221100 |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
Introduction:
DIN 1.4938 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.1.4938 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.1.4938 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
| DIN | W-Nr | Other |
|---|---|---|
| X12CrNiMoV12-3 | W-Nr 1.4938 | 1.4939 |
Chemical Composition (Mass weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| 0.08 ～ 0.15 | ≤ 0.50 | 0.40 ～ 0.90 | ≤ 0.025 | ≤ 0.015 | 11.0 ～ 12.5 | 2.00 ～ 3.00 | 1.50 ～ 2.00 | V 0.25 ～ 0.40 V 0.010 ～ 0.040 |
Mechanical Properties under room temp.
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | - | - | - | - | - | - |
| Q/T | 950 ～ 1150 | ≥ 800 | ≥ 13.0 | - | ≥ 55 | - |