X19CrMoNbVN11-1
| Product parameters | |
| Material Category:: | Steels of Blade |
| Steel Grade: | X19CrMoNbVN11-1 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN 17442,17744, DIN EN 10302, 10095, EN 10088-1 (2005) |
| Place of Origin: | Germany |
Description
TECHNICAL DATA SHEET - DIN X19CrMoNbVN11-1
MATERIAL CATEGORY - Martensitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 10.0 ~ 11.5
Ni (％): 0.20 ~ 0.60
Mo (％): 0.50 ~ 0.80
Al (%): ≤ 0.020
V (%): 0.10 ~ 0.30
W (%): -
Nb (%): 0.25 ~ 0.55
N (％): 0.05 ~ 0.10
B (%): ≤ 0.0015
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: heat treatment
Tensile strength, σb/MPa: 950 ~ 1150
Yield strength, σs≥/MPa: 780 min.
Elongation, δ5≥(％): 10.0
Non-scale temperature in Air: -℃
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W80 - 1200mm X L1000 - 4000mm
Sheet steel via cold rolled: T0.5 - 6mm X W30 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL CATEGORY - Martensitic creep-resisting steels
FEATURES AND CLASSIFICATIONS
MATERIAL SPECIFICATIONS - DIN 17442,17744, DIN EN 10302, 10095, EN 10088-1 (2005)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.50
Mn (％): 0.40 ~ 0.90
P (％)≤: 0.025
S (％)≤: 0.015
Cr (％): 10.0 ~ 11.5
Ni (％): 0.20 ~ 0.60
Mo (％): 0.50 ~ 0.80
Al (%): ≤ 0.020
V (%): 0.10 ~ 0.30
W (%): -
Nb (%): 0.25 ~ 0.55
N (％): 0.05 ~ 0.10
B (%): ≤ 0.0015
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: heat treatment
Tensile strength, σb/MPa: 950 ~ 1150
Yield strength, σs≥/MPa: 780 min.
Elongation, δ5≥(％): 10.0
Non-scale temperature in Air: -℃
APPLICATION FIELD
Heat-resistant steel is widely used in the field of manufacturing the boiler, steam turbine, motive power machine, industrial furnace, and other mechanical parts of aviation, petrochemical engineering operating at high temperature. Those parts must hold the features: high temperature strength, resistance to high temperature oxide etch, enough toughness, excellent machinability, weldability, structure stability based on different usages.
FORMS AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W80 - 1200mm X L1000 - 4000mm
Sheet steel via cold rolled: T0.5 - 6mm X W30 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.