1.3570
Description 1.3570 datasheet, 1.3570 Chemical, 1.3570 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military
| Product parameters | |
| Material Category:: | Structure Steel |
| Steel Grade: | 1.3570 |
| Material Technical Standards:: | EN |
| Specification Code:: | EN ISO 683-17 |
| Place of Origin: | EU |
Description
TECHNICAL SPECIFICATIONS - 1.3570
Official Test Certificate Report: issued by TUV - SGS - BV
MATERIAL TYPE: Case hardening bearing steel
MATERIAL STANDARDS: ISO 683/17
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.40
Mn (％): 0.65 ~ 1.10
P (％)≤: 0.025
S (％)≤: 0.015
Cr (%): 0.40 ~ 0.75
Mo (%): 0.10 ~ 0.20
Ni (%): -
Other (%): Cu ≤0.30, Al ≤0.050
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: + A = annealing
Hardness /≤HBW: 207
Condition: + AC = Spheroidizing annealing
Hardness /≤HBW: 170
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF /followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1200mm X L1000 - 5000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineer, Email: sales@cnlhss.com.
Official Test Certificate Report: issued by TUV - SGS - BV
MATERIAL TYPE: Case hardening bearing steel
MATERIAL STANDARDS: ISO 683/17
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.17 ~ 0.23
Si (％): ≤ 0.40
Mn (％): 0.65 ~ 1.10
P (％)≤: 0.025
S (％)≤: 0.015
Cr (%): 0.40 ~ 0.75
Mo (%): 0.10 ~ 0.20
Ni (%): -
Other (%): Cu ≤0.30, Al ≤0.050
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: + A = annealing
Hardness /≤HBW: 207
Condition: + AC = Spheroidizing annealing
Hardness /≤HBW: 170
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF /followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 - 1200mm X L1000 - 5000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.