1.4528
Specifications 1.4528 Datasheet, 1.4528 Chemical, 1.4528 Property from Steelmaking (EF / VIM), ESR & VAR technique, Blooming, Hot forging / rolling, Heat treat, Straighted, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materi
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | 1.4528 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312 |
| Place of Origin: | Germany |
Description
TECHNICAL DATA SHEET - DIN/EN 1.4528
HS CODE - 72222000 / 72221100
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Stainless steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.00 ~ 1.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 16.5 ~ 18.5
Ni (％): -
Mo (%): 1.00 ~ 1.50
Co (%): 1.30 ~ 1.80
V (%): 0.07 ~ 0.12
MECHANICAL PROPERTY UNDER ROOM TEMP.
Annealing temp.: 800 ~ 850, furnace cooled
Tensile strength, σb/ ≥ MPa: -
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 285 Max.
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS & SIZES
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@cnlhss.com
HS CODE - 72222000 / 72221100
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Stainless steel bar and forgings
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.00 ~ 1.10
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 16.5 ~ 18.5
Ni (％): -
Mo (%): 1.00 ~ 1.50
Co (%): 1.30 ~ 1.80
V (%): 0.07 ~ 0.12
MECHANICAL PROPERTY UNDER ROOM TEMP.
Annealing temp.: 800 ~ 850, furnace cooled
Tensile strength, σb/ ≥ MPa: -
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 285 Max.
METHOD OF MELT PROCESS
The alloy is usually produced by EF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
FORMS & SIZES
Round bar (Diameter): 5.5 ~ 350mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 500mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@cnlhss.com