Inconel 700
Specifications Inconel 700 datasheet, Inconel 700 Chemical, Inconel 700 Properties Steelmaking (EF / VIM ), ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined.
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | Inconel 700 |
| Place of Origin: | USA |
Description
TECHNICAL DATA SHEET - Grade Inconel alloy 700
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Nickel base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.035
S (％) ≤: 0.010
Cr (％): 13.0 ~ 17.0
Ni (％): 43.0 ~48.5
Mo (%): 3.20 ~4.50
Co (％): 26.5 ~ 30.0
W (%): -
Al (%): 2.50 ~ 4.00
Cu (%): ≤ 0.10
Ti (%): 1.80 ~2.80
Fe (%): ≤ 1.50
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 650
Yield strength, σ0.2/MPa: 315
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@cnlhss.com) our qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - Nickel base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 0.50
Mn (％): ≤ 0.50
P (％) ≤: 0.035
S (％) ≤: 0.010
Cr (％): 13.0 ~ 17.0
Ni (％): 43.0 ~48.5
Mo (%): 3.20 ~4.50
Co (％): 26.5 ~ 30.0
W (%): -
Al (%): 2.50 ~ 4.00
Cu (%): ≤ 0.10
Ti (%): 1.80 ~2.80
Fe (%): ≤ 1.50
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb/≥ MPa: 650
Yield strength, σ0.2/MPa: 315
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.