AMS 5649 / J92200 / AISI 316FM Free-machining Steels
| Product parameters | |
| Material Category:: | Austenitic Stainless Steel |
| Material Technical Standards:: | AMS 5649G |
| Place of Origin: | P.R. China |
| Melting Process Route:: | BEF + AOD / +ESR |
| Product Shapes:: | Round bars, flat bars, plate |
| Production Lead Time:: | Within 65 days after 40% deposit prepayable |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Basic Electric Furnace (EAF, AOD), it is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
These products have been used typically for Nuts and other parts requiring both Corrosion and heat resistance up to 1600 °F (871°C).
MAIN CHEMICAL COMPOSITIONS (Mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): 1.00 ~ 2.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％)≤: 0.20
Sulfur, S (％)≤: 0.10 ~ 0.20
Chromium, Cr (％): 17.0 ~ 19.0
Nickel, Ni (％): 12.0 ~ 14.0
Molybdenum, Mo (%): 1.75 ~ 2.50
Copper, Cu (%): ≤ 0.75
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Shapes: bars and forgings
Tensile strength, σb/MPa: 550
Tensile strength, σb/MPa: 862 max. (wire rod)
Yield strength, σ0.2/MPa: -
Elongation, δ(％): 35.0
Reduction of area, ф (％): 40.0
Hardness under aged condition | HBW: -
Hardness under solution condition | HBW: 255 Max.