AMS 5650 / SAE 30309S Austenitic Stainless Steel
| Product parameters | |
| Material category:: | Austenitic Stainless Steel |
| Material technical standards:: | AMS 5650E |
| Product shapes:: | Round bars, flat bars, plate |
| Standard export packing way:: | Wooden box, pallet / tray free from fumigation |
| Production lead time:: | Within 65 days after 40% deposit prepayable |
| Company ISO register No.:: | UQ211218R0 |
Description
These products have been used typically for parts requiring both Corrosion and heat resistance up to 1093°C.
Main Chemical Elements (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 2.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 12.0 ~ 15.0
Molybdenum, Mo (%): ≤ 0.75
Copper, Cu (%): ≤ 0.75
Typical Mechanical Properties.
Tensile strength, σb/MPa: 515
Tensile strength, σb/MPa: 862 max. (wire rod)
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 40.0
Reduction of area, ф (％): -
Hardness under aged condition | HBW: -
Hardness under solution condition | HBW: 187 Max.
Main Chemical Elements (mass weight %)
Carbon, C (％): ≤ 0.08
Manganese, Mn (％): ≤ 2.00
Silicon, Si (％): ≤ 1.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 22.0 ~ 24.0
Nickel, Ni (％): 12.0 ~ 15.0
Molybdenum, Mo (%): ≤ 0.75
Copper, Cu (%): ≤ 0.75
Typical Mechanical Properties.
Tensile strength, σb/MPa: 515
Tensile strength, σb/MPa: 862 max. (wire rod)
Yield strength, σ0.2/MPa: 205
Elongation, δ(％): 40.0
Reduction of area, ф (％): -
Hardness under aged condition | HBW: -
Hardness under solution condition | HBW: 187 Max.