TECHNICAL DATA SHEET - Grade EN 58H
MATERIAL CATEGORY - Stainless steel 18%Cr / 10%Ni / 2%Mo
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): 0.07 ~ 0.16
Mn (％): 1.70 ~ 2.50
Si (％): 0.15 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 9.00 ~ 12.0
Mo (%): 1.50 ~ 2.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 520
Yield strength, σ0.2/≥ MPa: 245
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 550mm
Rolled / forged plate: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com.
MATERIAL CATEGORY - Stainless steel 18%Cr / 10%Ni / 2%Mo
TECHNICAL SPECIFICATION - BS970 Part 6
MELTING PROCESS - Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS ( Mass Weight - %)
C (％): 0.07 ~ 0.16
Mn (％): 1.70 ~ 2.50
Si (％): 0.15 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.025
Cr (%): 17.0 ~ 20.0
Ni (%): 9.00 ~ 12.0
Mo (%): 1.50 ~ 2.50
MECHANICAL PROPERTY UNDER ROOM TEMP.
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 520
Yield strength, σ0.2/≥ MPa: 245
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB269
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Round bar: 5.5mm to 500mm
Square bar / Flat bar: 10mm to 550mm
Rolled / forged plate: 10mm to 550mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.