TECHNICAL DATA SHEET - ASTM A182 Grade F45
MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 21Cr-11Ni-2Si Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.05 ~ 0.10
Mn (％): ≤ 0.80
Si (％): 1.40 ~ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Ni (%): 10.0 ~ 12.0
Cr (%): 20.0 ~ 22.0
Mo (%): -
N (%): 0.14 ~ 0.20
Ce (%): 0.03 ~ 0.08
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 600
Yield strength, σ0.2/MPa: 310
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1040 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry or help, pleased to E-mail our resident team of qualified production engineers, Email: sales@cnlhss.com
MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 21Cr-11Ni-2Si Austenitic Stainless steel
Customs HS Code - 72221100 / 72221900
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.05 ~ 0.10
Mn (％): ≤ 0.80
Si (％): 1.40 ~ 2.00
P (％)≤: 0.040
S (％)≤: 0.030
Ni (%): 10.0 ~ 12.0
Cr (%): 20.0 ~ 22.0
Mo (%): -
N (%): 0.14 ~ 0.20
Ce (%): 0.03 ~ 0.08
MECHANICAL PROPERTY UNDER ROOM TEMP.
Forms: Round bar, flat bar, forgings and plate
Tensile strength, σb/≥ MPa: 600
Yield strength, σ0.2/MPa: 310
Elongation, δ ≥(％): 35.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing 1040 Deg. C (+AT)
Cooling medium: water or oil cooling
Tempering temperature: -
MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm ~ 500mm
Square bar / Flat bar: 10mm to 1000mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.