1.4542 forgings, 17-4PH ring, AISI 630 tube
EN 1.4542 is A Precipitation Hardening Martensitic Stainless steel with an addition of Nb/Cu elements. Grade 1.4542 Combines High Strength, hardness (up to HRC40), and corrosion resistance.
| Product parameters | |
| Material Category:: | Precipitation hardening Stainless Steel |
| Stocklist & Inventory Available:: | Diameter 10 ~ 240mm |
| Melting Process Route:: | EAF + VD + LF / BEF + ESR |
| Min. order quantity Per Batch:: | 200 KG |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 5 days after 30% downpayment. |
Description
Introduction:
1.4542 is a corrosion resistant grade which is soft and ductile in the solution annealed condition. Medium to high strength, good toughness and strength is obtained by the appropriate ageing treatment. As a martensitic precipitation hardening stainless it is characterised by high tensile strength and high yield strength obtained by solution annealing, followed by a single or double low temperature age hardening treatment. 1.4542 has corrosive properties comparable to 304 austenitic stainless steel in many environments.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace. 1.4542 is used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Technical Standard: DIN EN 10088-1
All Grades Comparison
| DIN | ASTM | AISI | UNS | JIS | Other |
|---|---|---|---|---|---|
| 1.4542 X5CrNiCuNb16-4 |
Grade 630 | 630 | S17400 | SUS 630 | 17-4PH AMS 5643 AMS 5622 Z6CNU17-04 10705GU-GV |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.07 | ≤ 1.00 | ≤ 1.00 | ≤ 0.040 | ≤ 0.030 | 15.0 ～ 17.0 | 3.00 ～ 5.00 | - | Cu 3.00 ～ 5.00 Nb+Ta 0.15 ～ 0.45 |
Mechanical Properties Under Room Temperature
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealed | ≤ 1034 | ≤ 650 | 6.0 ～ 15.0 | 30.0 ～ 60.0 | - | ≤ 363 |
| H900 | ≥ 1380 | ≥ 1275 | ≥ 14.0 | ≥ 50.0 | ≥ 20 | ≤ 420 |
| H925 | ≥ 1310 | ≥ 1200 | ≥ 14.0 | ≥ 54.0 | ≥ 34 | ≤ 409 |
| H1025 | ≥ 1170 | ≥ 1140 | ≥ 15.0 | ≥ 56.0 | ≥ 47 | ≤ 352 |
| H1075 | ≥ 1140 | ≥ 1035 | ≥ 16.0 | ≥ 58.0 | ≥ 61 | ≤ 341 |
| H1100 | ≥ 1035 | ≥ 930 | ≥ 17.0 | ≥ 58.0 | ≥ 61 | ≤ 332 |
| H1150 | ≥ 1000 | ≥ 860 | ≥ 19.0 | ≥ 60.0 | ≥ 68 | ≤ 311 |
| H1150+H1150 | ≥ 965 | ≥ 760 | ≥ 20.0 | ≥ 60.0 | ≥ 108 | ≤ 302 |
| H1150M | ≥ 860 | ≥ 585 | ≥ 22.0 | ≥ 68.0 | ≥ 135 | ≤ 277 |
Shapes and Dimensions Available
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.