STAINLESS STEEL DATASHEET - Grade 153Ma
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: 18Cr - 9Ni - N austenitic stainless
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.06
Si (％): 1.00 ~ 2.00
Mn (％): ≤ 0.80
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ~ 19.0
Ni (％): 9.00 ~ 10.0
Mo (％): -
N (%): 0.12 ~ 0.18
Ce (%): 0.03 ~ 0.08
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution treatment
Thickness/mm: 160max.
Tensile strength, σb/MPa: 600
Yield strength, σ0.2≥/MPa: 290
Elongation, δ5≥(％): 40.0
Reduction of area, ψ≥(％): -
Akv≥/J: -
Hardness HBS: 217
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + A
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip & rolled plate: T0.1 - 150mm X W5 - 1500mm X Random length (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@cnlhss.com) our qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: 18Cr - 9Ni - N austenitic stainless
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.04 ~ 0.06
Si (％): 1.00 ~ 2.00
Mn (％): ≤ 0.80
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 18.0 ~ 19.0
Ni (％): 9.00 ~ 10.0
Mo (％): -
N (%): 0.12 ~ 0.18
Ce (%): 0.03 ~ 0.08
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution treatment
Thickness/mm: 160max.
Tensile strength, σb/MPa: 600
Yield strength, σ0.2≥/MPa: 290
Elongation, δ5≥(％): 40.0
Reduction of area, ψ≥(％): -
Akv≥/J: -
Hardness HBS: 217
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + A
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip & rolled plate: T0.1 - 150mm X W5 - 1500mm X Random length (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.