17-22AV
Description 17-22AV datasheet, 17-22AV Chemical, 17-22AV Properties Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military s
| Product parameters | |
| Material Category:: | Superalloy |
| Steel Grade: | 17-22AV |
| Material Technical Standards:: | AMS |
| Specification Code:: | AMS 6436B |
| Place of Origin: | USA |
Description
TECHNICAL DATA SHEET - Grade 17-22AV
MATERIAL CATEGORY - Low alloy steel with high tensile
TECHNICAL SPECIFICATION - AMS 6436B
MELTING: Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.20 ~ 0.25
Mn (％): 0.60 ~ 0.90
Si (％): 0.55 ~ 0.75
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): 1.00 ~ 1.50
V (%): 0.75 ~ 0.95
Mo (%): 0.40 ~ 0.60
Ni (%): ≤ 0.25
Cu (%): ≤ 0.35
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: -
Tempering temperature /℃: -
Tensile strength,σb/≥ MPa: 985
Yield strength, σ0.2/≥ MPa: 785
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥(％): 50
Hardness in condition of annealing +A: HB229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Strip: THK 0.3 ~ 3.0 X Width 10 ~ 300mm
Sheet: THK 0.3 ~ 10 X Width 10 ~ 1000mm
Wire rod: Diameter 0.4 ~ 3.0mm
Round bar (diameter): 5.5 ~ 450mm
sales@cnlhss.com.
MATERIAL CATEGORY - Low alloy steel with high tensile
TECHNICAL SPECIFICATION - AMS 6436B
MELTING: Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.20 ~ 0.25
Mn (％): 0.60 ~ 0.90
Si (％): 0.55 ~ 0.75
P (％)≤: 0.025
S (％)≤: 0.025
Cr (%): 1.00 ~ 1.50
V (%): 0.75 ~ 0.95
Mo (%): 0.40 ~ 0.60
Ni (%): ≤ 0.25
Cu (%): ≤ 0.35
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: -
Tempering temperature /℃: -
Tensile strength,σb/≥ MPa: 985
Yield strength, σ0.2/≥ MPa: 785
Elongation, δ ≥(％): 10.0
Reduction of area, ф ≥(％): 50
Hardness in condition of annealing +A: HB229 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
AVAILABLE FORMS & DIMENSIONS
Strip: THK 0.3 ~ 3.0 X Width 10 ~ 300mm
Sheet: THK 0.3 ~ 10 X Width 10 ~ 1000mm
Wire rod: Diameter 0.4 ~ 3.0mm
Round bar (diameter): 5.5 ~ 450mm
sales@cnlhss.com.