AMS 5719 Round bar, Flat bar Available
Specifications AMS 5719 datasheet, AMS 5719 Chemical, AMS 5719 Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these mater
| Product parameters | |
| Material Category:: | Martensitic Stainless Steel Series |
| Steel Grade: | AMS 5719C |
| Terms of Price:: | Ex works, CIF, CFR |
| Stocklist & Inventory Available:: | Diameter 50 ~ 230mm |
| Min. order quantity Per Batch:: | 200 KG |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 5 days after 30% deposit prepayable |
| Company ISO Register No:: | UQ211218R0 |
Description
AEROSPACE MATERIAL SPECIFICATION - Grade AMS 5719
TECHNICAL SPECIFICATIONS - AMS 5719C
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
C (％): 0.08 ~ 0.13
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Mo (％): 1.50 ~ 2.00
Ni (%): 2.00 ~ 3.00
V (％): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb≥ /MPa: 1100
Yield strength, σs≥ /Mpa: 860
Elongation, δ5 ≥(%): 12.0
Hardness HBW: 341 ~ 375
Hardness HBS: 310 max in annealed condition
HEAT TREATMENT PRACTICE
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
TECHNICAL SPECIFICATIONS - AMS 5719C
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
C (％): 0.08 ~ 0.13
Si (％): ≤ 0.35
Mn (％): 0.50 ~ 0.90
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 11.0 ~ 12.5
Mo (％): 1.50 ~ 2.00
Ni (%): 2.00 ~ 3.00
V (％): 0.25 ~ 0.40
N (%): 0.01 ~ 0.05
TYPICAL MECHANICAL PROPERTIES
Tensile strength, σb≥ /MPa: 1100
Yield strength, σs≥ /Mpa: 860
Elongation, δ5 ≥(%): 12.0
Hardness HBW: 341 ~ 375
Hardness HBS: 310 max in annealed condition
HEAT TREATMENT PRACTICE
Annealed: 691° C (+/-11) for 6 hours min followed by air cool
Hardened:1052° C (+/-) for 30 mins followed by oil quench
1st Tempered: 560-590° C for 1 hour min followed by air cool
2nd Tempered: 538-560° C for 3 hours min followed by air cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.