STEEL MATERIAL DATA SHEET - AISI 330
MATERIAL CATEGORY: 19Cr-36Ni Austenitic steel
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632, A176, A580
Alloy 330 is an austenitic heat and corrosion resisting alloy which has an exceptional combination of strength and resistance to carburization, oxidation and thermal shock.
Alloy 330 is used in a wide range of applications in high temperature industrial environments
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 17.0 ~ 20.0
Ni (％): 34.0 ~ 37.0
Mo (％): ≤ 0.75
Others (%): Cu ≤0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Plate,sheet, strip, forge piece, wire rod
Condition: annealed
Tensile strength, σb/MPa: 670
Yield strength, σ0.2/MPa: 240
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness | HRB≤: 95
Cold bending property: N
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE AND FORMS
Round bar / Wire rod (Diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 600mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com
MATERIAL CATEGORY: 19Cr-36Ni Austenitic steel
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632, A176, A580
Alloy 330 is an austenitic heat and corrosion resisting alloy which has an exceptional combination of strength and resistance to carburization, oxidation and thermal shock.
Alloy 330 is used in a wide range of applications in high temperature industrial environments
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 17.0 ~ 20.0
Ni (％): 34.0 ~ 37.0
Mo (％): ≤ 0.75
Others (%): Cu ≤0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Plate,sheet, strip, forge piece, wire rod
Condition: annealed
Tensile strength, σb/MPa: 670
Yield strength, σ0.2/MPa: 240
Elongation, δ(％): 30.0
Reduction of area, ф(％): -
Hardness | HRB≤: 95
Cold bending property: N
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE AND FORMS
Round bar / Wire rod (Diameter): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 600mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com