UNS S31008 - AMS 5651 Austenitic Steel Forgings
Product parameters | |
Material Category:: | Austenitic Stainless Steel |
Material Technical Standards:: | ASTM A276, ASTM A240 |
Place of Origin: | P. R. China |
Terms of Price:: | Ex works, CIF, and CFR |
Stocklist & Inventory Available:: | Round bar Diam. 50mm / 62mm / 122mm |
Min. order quantity Per Batch:: | 1500 KG |
Certification:: | Commercial Invoice, Packing list, CO, Bill of lading, Origin of Certificate, Form E |
Product Shapes:: | Round bar, Flat bar, Plate |
Customs HS code:: | 72222000 / 72223000 |
Heat Treatment Practice:: | Solution annealed 1040 ℃, water or air cooled. |
Ultrasonic Test Standard:: | / GB/T 4162 / EN 10228-3 / EN 10308. |
Production Lead Time:: | Within 15 days after 30% downpayment. |
Unified Social Credit Code:: | 91510871777942750J |
Company ISO Register No:: | UQ211218R0 |
Description
Technical Data Sheet
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Shapes and dimensions:
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM
C (%) | ≤ 0.08 |
Si(%) | ≤ 1.50 |
Mn(%) | ≤ 2.00 |
P(%) | ≤ 0.045 |
S (%) | ≤ 0.030 |
Cr (%) | 24.0 ~ 26.0 |
Ni (%) | 19.0 ~ 22.0 |
Mo(%) | - |
Other (%) | - |
Condition of heat treatment | - |
Tensile Rm (MPa) | 515 |
Yield Rp0.2 (MPa) | 205 |
Elongation A (%) | 40 |
Reduction in cross section on fracture Z (%) | - |
Impact AKV/AKU (J) | - |
Brinell Hardness (HBW) | 217 max |