ASTM A182 Gr.S31653
Specification ASTM A890 Gr.4A datasheet, ASTM A890 Gr.4A Chemical, A890 Grade 4A properties from steelmaking,hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | ASTM A182 Gr.S31653 |
| Material Technical Standards:: | ASTM |
| Specification Code:: | ASTM A182 - 2018 |
| Place of Origin: | USA |
Description
TECHNICAL DATA SHEET - ASTM A182 Grade S31653
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 17Cr - 13Ni Austenitic Stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Mn (％): ≤ 2.00
Si (％): ≤ 0.40
P (％)≤: 0.035
S (％)≤: 0.020
Cr (%): 16.0 ~ 18.0
Mo (%): 2.00 ~ 3.00
Ni (%): 11.0 ~ 14.0
Nb (%): -
Ti (%): -
N (%): 0.10 ~ 0.16
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling
Tempering temperature: 1040 Deg.C
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to E-mail (sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL TECHNICAL STANDARDS: ASTM A182 - 2018
MATERIAL TYPE: 17Cr - 13Ni Austenitic Stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Mn (％): ≤ 2.00
Si (％): ≤ 0.40
P (％)≤: 0.035
S (％)≤: 0.020
Cr (%): 16.0 ~ 18.0
Mo (%): 2.00 ~ 3.00
Ni (%): 11.0 ~ 14.0
Nb (%): -
Ti (%): -
N (%): 0.10 ~ 0.16
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 515
Yield strength, σ0.2/MPa: 205
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: -
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling
Tempering temperature: 1040 Deg.C
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to E-mail (sales@cnlhss.com) our resident team of qualified production engineers.