X2CrNi19-11 Austenitic Type Stainlesss Steel
| Product parameters | |
| Material Category:: | Austenitic Stainless Steel |
| Place of Origin: | P. R. China |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Round bar Diam. 25 ~ 120mm |
| Min. order quantity Per Batch:: | 500 KG |
| Certification:: | Commercial Invoice, Packing list, CO, Bill of lading, Origin of Certificate, Form E |
| Product Shapes:: | Round bar, Flat bar, Hollow bar, Plate, and Forgings. |
| Surface Condition:: | Peeled - Rough turned - Bright surface. |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308. |
| Standard Export Packing Way:: | Wooden box, wooden Pallet / tray with free from fumigation. |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
X2CrNi19-11 is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X2CrNi19-11 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X2CrNi19-11 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
| DIN | W-Nr |
|---|---|
| X2CrNi19-11 | W-Nr 1.4306 |
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.030 | ≤ 1.00 | ≤ 2.00 | ≤ 0.045 | ≤ 0.030 | 18.0 ～ 20.0 | 10.0 ～ 12.0 | - | N ≤ 0.11 |
Mechanical Properties At RM
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | - | - | - | - | - | - |
| Q/T | 460 ～ 680 | ≥ 180 | ≥ 45.0 | - | - | ≤ 215 |
Forms and Dimensions:
Round bar (Diameter): 5.5 mm to 700 mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.