MATERIAL DATA SHEET - E-Z5CNU15
MATERIAL CATEGORY - Precipitation hardening type 15Cr-5Ni-4Cu
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): -
Cu (％): 2.50 ~ 4.50
Nb+Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Form: Bar, forge piece
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 700mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 1.0mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com.
MATERIAL CATEGORY - Precipitation hardening type 15Cr-5Ni-4Cu
MATERIAL SPECIFICATIONS
ASTM A959 (2004), A276, A312, A632
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment + Aged
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): -
Cu (％): 2.50 ~ 4.50
Nb+Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER FINAL HEAT TREATMENT
Form: Bar, forge piece
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 700mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 1.0mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@cnlhss.com.