TECHNICAL DATA SHEET - ASTM A182 Grade F72
MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 18Cr-15Ni-3Mo Austenitic Stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Mn (％): ≤ 1.00
Si (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (%): 17.5 ~ 19.0
Ni (%): 14.5 ~ 16.5
Mo (%): 3.80 ~ 4.50
Cu (%): 2.80 ~ 4.00
Nb (%): -
Ti (%): -
N (%): 0.15 ~ 0.21
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 550
Yield strength, σ0.2/MPa: 245
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: 217
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling
Tempering temperature: 1080 ~ 1180 Deg.C
PRODUCT MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to E-mail (sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL TECHNICAL STANDARDS - ASTM A182 - 2018
MATERIAL TYPE - 18Cr-15Ni-3Mo Austenitic Stainless steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Mn (％): ≤ 1.00
Si (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.020
Cr (%): 17.5 ~ 19.0
Ni (%): 14.5 ~ 16.5
Mo (%): 3.80 ~ 4.50
Cu (%): 2.80 ~ 4.00
Nb (%): -
Ti (%): -
N (%): 0.15 ~ 0.21
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 550
Yield strength, σ0.2/MPa: 245
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): 50.0
Hardness via heat treatment /HBW: 217
HEAT TREATMENT PRACTICE
Condition: solution annealing
Cooling medium: water or oil cooling
Tempering temperature: 1080 ~ 1180 Deg.C
PRODUCT MELTING & AVAILABLE DIMENSIONS
The alloy is usually produced by BEF & BEF + AOD & EAF + VD + LF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' specific requirements.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 ~ 400mm X W60 ~ 1000mm X L1000 ~ 3500mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical inquiry, pleased to E-mail (sales@cnlhss.com) our resident team of qualified production engineers.