Specifications K91456, Ex-stock K91456 Chemical, K91456 properties steelmaking,Grade K91456 Electroslag remelting, blooming, Ultrasonic testing, Hot forging & Rolling, Heat treatment, Cold working, Straightening.
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | K91456 |
| Material Technical Standards:: | SAE |
| Specification Code:: | SAE AMS 5623A |
| Place of Origin: | USA |
Description
TECHNICAL DATA SHEET - Grade K91456
MATERIAL CATEGORY: Aerospace "S" Series steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: SAE AMS 5623A
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.55 ~ 0.65
Si (％): ≤ 1.00
Mn (％): 5.00 ~ 6.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): -
Ni (％): 8.50 ~ 10.5
Mo (％): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution annealed
Condition: work hardened
Tensile strength σb≥/MPa: -
Yield strength σs≥/MPa: -
Elongation δ5≥(%): -
AKV≥/J: -
Hardness HBS: 149 ~ 179
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution anneal treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@cnlhss.com.
MATERIAL CATEGORY: Aerospace "S" Series steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: SAE AMS 5623A
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.55 ~ 0.65
Si (％): ≤ 1.00
Mn (％): 5.00 ~ 6.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): -
Ni (％): 8.50 ~ 10.5
Mo (％): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution annealed
Condition: work hardened
Tensile strength σb≥/MPa: -
Yield strength σs≥/MPa: -
Elongation δ5≥(%): -
AKV≥/J: -
Hardness HBS: 149 ~ 179
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution anneal treatment