MATERIAL TECHNICAL DATA SHEET - UNS N07090
MATERIAL CATEGORY - Nickel-Chromium-Cobalt alloy
AVAILABILITY - Round bar / flat bar / steel strip / square bar / ring / valve body / forge piece
MATERIAL SPECIFICATIONS - Alloy 90, W-Nr 2.4632, AMS 5829, EN 2400, NCK 20D
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.13
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Balance
Ti(％): 2.00~3.00
Al (%): 1.00 ~ 2.00
Co (%): 15.0 ~ 21.0
Other(％): Cu ≤0.20, Fe ≤1.50, B ≤0.02, Zr ≤0.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution annealed
Tensile strength, σb/MPa: 800~1000
Yield strength, σ0.2≥/MPa: -
Elongation, δ5 ≥(％): -
Reduction of area, ψ≥(％): -
Hardness≥: -
Condition: solution annealed + aged
σb/MPa: 1300~1400
σ0.2≥/MPa: -
δ5≥(％): -
ψ≥(％): -
Hardness≥: -
PRODUCT DESCRIPTION
The
alloy
is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Wrought Ni-Cr alloy strengthened by the addition of Ti and Al. Age hardenable and creep-resistant alloy for service at temperatures to 920°C.
Density 8.18 gm/cc
Melting point: 1370 °C
HEAT TREATMENT PRACTICE
Annealing - Age Harden at 750°C (1380°F) for 4 hours and air cool.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Gas turbine engineering
Automobile exhaust valves
Die-casting inserts and cores
Nuclear boiler tube parts.
Driveshafts
Gears
Fasteners
Landing and takeoff gear
Missile and ejector systems
Torsion springs
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@cnlhss.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
MATERIAL CATEGORY - Nickel-Chromium-Cobalt alloy
AVAILABILITY - Round bar / flat bar / steel strip / square bar / ring / valve body / forge piece
MATERIAL SPECIFICATIONS - Alloy 90, W-Nr 2.4632, AMS 5829, EN 2400, NCK 20D
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.13
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.020
S (％)≤: 0.015
Cr (％): 18.0 ~ 21.0
Ni (％): Balance
Ti(％): 2.00~3.00
Al (%): 1.00 ~ 2.00
Co (%): 15.0 ~ 21.0
Other(％): Cu ≤0.20, Fe ≤1.50, B ≤0.02, Zr ≤0.15
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: solution annealed
Tensile strength, σb/MPa: 800~1000
Yield strength, σ0.2≥/MPa: -
Elongation, δ5 ≥(％): -
Reduction of area, ψ≥(％): -
Hardness≥: -
Condition: solution annealed + aged
σb/MPa: 1300~1400
σ0.2≥/MPa: -
δ5≥(％): -
ψ≥(％): -
Hardness≥: -
PRODUCT DESCRIPTION
The
alloy
is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QT
Wrought Ni-Cr alloy strengthened by the addition of Ti and Al. Age hardenable and creep-resistant alloy for service at temperatures to 920°C.
Density 8.18 gm/cc
Melting point: 1370 °C
HEAT TREATMENT PRACTICE
Annealing - Age Harden at 750°C (1380°F) for 4 hours and air cool.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Gas turbine engineering
Automobile exhaust valves
Die-casting inserts and cores
Nuclear boiler tube parts.
Driveshafts
Gears
Fasteners
Landing and takeoff gear
Missile and ejector systems
Torsion springs
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@cnlhss.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1000mm X L1000 - 12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.