NCF800H
| Product parameters | |
| Material Category:: | Superalloy |
| Steel Grade: | NCF800H |
| Material Technical Standards:: | JIS |
| Specification Code:: | JIS G4901 -1999, JIS G 4902-1991 |
| Place of Origin: | Japan |
Description
Introduction:
NCF800H usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
NCF800H usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
NCF800H Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine, turbine blade
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
All Grades Comparison
NCF800H Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
Heat treating fixture
Nuclear reactor
Turbine engine parts - mechanical gears, gear shaft, main axis, blade
Mechanical parts - bolt and nut, fastener
Gas turbine, turbine blade
Fuel nozzle
Heat treatment furnace flask and components, especially in the carbonization.
These materials must stand up to high heat, extreme oxidation potential and recycling.
| JIS | Other |
|---|---|
| NCF800H | - |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| 0.05 ～ 0.10 | ≤ 1.00 | ≤ 1.50 | ≤ 0.030 | ≤ 0.015 | 19.0 ～ 23.0 | 30.0 ～ 35.0 | - | Cu ≤ 0.75 Al 0.15 ～ 0.60 Ti 0.15 ～ 0.60 |
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | ≥ 590 | ≥ 240 | ≥ 30.0 | - | - | - |
| Solution treated | - | - | - | - | - | - |
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Length: Fixed length or random length or based on the customer's special requirement.
For all stock availability contact Sales.