PH13-8Mo
Specifications PH13-8Mo Datasheet, PH13-8Mo Chemical, PH13-8Mo Properties from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these mater
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | PH13-8Mo |
| Material Technical Standards:: | ASTM |
| Specification Code:: | ASTM A564 (2003) |
| Place of Origin: | USA |
Description
TECHNICAL SPECIFICATION DATASHEET - Grade PH13-8Mo
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Precipitation hardening stainless steel
MATERIAL SPECIFICATIONS - ASTM A564 (2003)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
N (%): ≤ 0.01
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)
Solution treatment temperature and cooling ways: 927 +/-15℃
Steel plate thickness /mm: 0.038~101.6
σb≥/MPa: -
σ0.2≥/MPa: -
δ≥(％): -
Hardness ≤|HRC: 38
Hardness ≤|HBS: 363
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution + ageing treated
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Automobile parts, exhaust pipe
Electronics
Turbine motor blade
Bolt and nut
Valve
Pressure vessel
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail us: sales@cnlhhs.com
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Precipitation hardening stainless steel
MATERIAL SPECIFICATIONS - ASTM A564 (2003)
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.05
Si (％): ≤ 0.10
Mn (％): ≤ 0.20
P (％)≤: 0.010
S (％)≤: 0.008
Cr (％): 12.3 ~ 13.2
Ni (％): 7.50 ~ 8.50
Mo (％): 2.00 ~ 2.50
Al (％): 0.90 ~ 1.35
N (%): ≤ 0.01
MECHANICAL PROPERTIES AFTER HEAT TREATMENT (SOLUTION TREATMENT)
Solution treatment temperature and cooling ways: 927 +/-15℃
Steel plate thickness /mm: 0.038~101.6
σb≥/MPa: -
σ0.2≥/MPa: -
δ≥(％): -
Hardness ≤|HRC: 38
Hardness ≤|HBS: 363
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution + ageing treated
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Automobile parts, exhaust pipe
Electronics
Turbine motor blade
Bolt and nut
Valve
Pressure vessel
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 3mm to 400mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail us: sales@cnlhhs.com