UNS S41800 Heat Resisting Valve Body
| Product parameters | |
| Material Category:: | Martensitic Hardening Stainless Steel |
| Place of Origin: | P. R. China |
| Product Shapes:: | Round bar, Flat bar, Plate, Wire rod, and Forging piece. |
| Heat Treatment Practice:: | Solution 1040 ℃, oil or air cooled, tempered 580 ℃ air cooled, double tempered. |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308. |
| Standard Export Packing Way:: | Wooden box, wooden Pallet / tray with free from fumigation. |
| Production Lead Time:: | Within 55 days after 40% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Main Chemical Composition (mass weight %)
C (％) 0.15 ～ 0.20, Si(％) ≤ 0.50, Mn(％) ≤ 0.50
P(％) ≤ 0.040, S (％) ≤ 0.030
Cr (％) 12.0 ～ 14.0 , Ni (％) 1.80 ～ 2.20 , Mo(％) ≤ 0.50
W (％) 2.50 ～ 3.50, Fe (%): remainder.
| Condition of heat treatment | - |
| Tensile Rm (MPa) | 965 |
| Yield Rp0.2 (MPa) | 760 |
| Elongation A (%) | 15 |
| Reduction in cross section on fracture Z (%) | 45 |
| Impact AKV/AKU (J) | - |
| Brinell Hardness (HBW) | - |
| Forms and dimensons Round bar (Diameter): 5.50 ~ 650mm Square bar / Flat bar: 3 ~ 650mm Wire rod (Diameter): 0.10 ~ 16mm Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form) Forging piece: Different shapes based on OEM |