Aquamet 17 Shaft, Rod, Bars
Specifications Aquamet 17 Datasheet - Ex-stock Chemical Properties Forging Bar Plate, Technical Specifications Melting, ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
| Product parameters | |
| Stocklist & Inventory Available:: | Diameter 85 ~ 130mm |
| Melting Process Route:: | EAF + VD + LF / BEF + ESR |
| Min. order quantity Per Batch:: | one piece |
| Certification:: | MTR, COC, Certificate of origin, Form A/E, Invoice, Packing list |
| Heat Treatment Practice:: | Solution annealed 1050 ℃, water, oil or air cooled, aged 620 ℃, air cooled |
| Surface Condition:: | Rough turned. |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Production Lead Time:: | Within 25 days after 40% deposit prepayable |
Description
AQUAMET 17 is A Precipitation Hardening Martensitic Stainless steel with an addition of Nb/Cu elements. It Combines High Strength, hardness (up to HRC40), and corrosion resistance.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 500mm
Forging piece: Different shapes based on OEM.
MATERIAL TECHNICAL DATA SHEET - Grade Aquamet 17
CHEMICAL COMPOSITION (MASS WEIGHT %)
C (％): ≤ 0.07, Si (％): ≤ 1.00, Mn (％): ≤ 1.00, P (％)≤: 0.040, S (％)≤: 0.030
Cr (％): 14.5 ~ 16.5, Ni (％): 3.00 ~ 5.00, Mo (％): -, Co (%): -, W (%): -, Al (%): -
Cu (%): 3.00 ~ 5.00, Nb (%): 0.15 ~ 0.45, Fe (%): remainder
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 725
Elonghation, δ ≥(％): 15.0
Reduction of area, ф ≥ (％): 45.0
Hardness | HB: