X6CrMoS17 / 1.4105 Ferritic Stainless Steel
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X6CrMoS17 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
| Product parameters | |
| Material Category:: | Stainless Steel |
| Material Technical Standards:: | DIN EN 10088-1, 10088-4, 10297, 10312 |
| Min. order quantity Per Batch:: | 3300 KG |
| Customs HS code:: | 72221100 |
| Heat Treatment Practice:: | Annealed 750 ~ 850℃, water or air cooled |
| Ultrasonic Test Standard:: | EN 10228-3, GB/T 4162-2008, ASTM E2375, ASTM A745. EN 10307-2001 |
| Production Lead Time:: | Within 55 days after 40% deposit prepayable |
Description
6CrMoS17 is usually produced by BEF & AOD.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X6CrMoS17 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X6CrMoS17 used for components such as fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Equivalent
| DIN | W-Nr |
|---|---|
| X6CrMoS17 | W-Nr 1.4105 |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.08 | ≤ 1.50 | ≤ 1.50 | ≤ 0.040 | 0.15～ 0.35 | 16.0 ～ 18.0 | - | 0.20 ～ 0.60 | - |
Typical Mechanical Properties
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | 430 ～ 630 | ≥ 250 | ≥ 20.0 | - | - | ≤ 220 |
| H/T | - | - | - | - | - | - |
Shapes & Dimensions Available
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.