Ex-stock STR 3, Specifications STR 3 Suppliers, STR 3 Forging Bar Plate machined, Grade STR 3 Exporters Technical specifications - KS D3731 - 2002 / 2007. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | STR 3 |
| Material Technical Standards:: | KS |
| Specification Code:: | KS D3731 - 2002/2007 |
| Place of Origin: | Korea |
Description
TECHNICAL DATA SHEET - KS D3731 Grade STR 3
TECHNICAL SPECIFICATIONS: KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.35 ~ 0.45
Si (％): 1.80 ~ 2.50
Mn (％): ≤ 0.60
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 10.0 ~ 12.0
Ni (％): ≤ 0.60
Mo (%): 0.70 ~ 1.20
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 800 ~ 900 Deg.C, slow cooling.
Tensile strength, σb/ ≥ MPa: 932
Yield strength, σ0.2/ ≥ MPa: 686
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 35.0
Hardness ≤ (HBW): 269 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
TECHNICAL SPECIFICATIONS: KS D3731 - 2002/2007
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel bar and plate
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.35 ~ 0.45
Si (％): 1.80 ~ 2.50
Mn (％): ≤ 0.60
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 10.0 ~ 12.0
Ni (％): ≤ 0.60
Mo (%): 0.70 ~ 1.20
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: anneal treated 800 ~ 900 Deg.C, slow cooling.
Tensile strength, σb/ ≥ MPa: 932
Yield strength, σ0.2/ ≥ MPa: 686
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 35.0
Hardness ≤ (HBW): 269 Min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (Thickness X Width): 10 ~ 400 X 15 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar