SUS631-CPS
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | SUS631-CPS |
| Material Technical Standards:: | JIS |
| Specification Code:: | JIS G4313-1996 |
| Place of Origin: | Japan |
Description
Introduction:
SUS631-CPS usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
SUS631-CPS usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.SUS631-CPS used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.SUS631-CPS used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
| JIS | Other |
|---|---|
| SUS631-CPS | - |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| ≤ 0.09 | ≤ 1.00 | ≤ 1.00 | ≤ 0.040 | ≤ 0.030 | 16.0 ～ 18.0 | 6.50 ～ 7.75 | - | Al 0.25 ～ 1.50 |
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| solution treated | ≥ 1030 | ≥ 380 | ≥ 20.0 | - | - | ≤ 229 |
| H900 hardened, aged 470~490 air cooled | ≥ 1140 | ≥ 960 | ≥ 5.0 | ≥ 25.0 | - | ≤ 363 |
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Length: Fixed length or random length or based on the customer's special requirement.
For all stock availability contact Sales.